| Max Speed | 250km/h |
|---|---|
| Electrical Insulation Resistance | ≥5 KΩ |
| Gauge Adjustment | ±10 Mm |
| Rail Pad Stiffness | Standard: 80‑120 KN/mm; High‑Elastic: 40‑60 KN/mm |
| Height Adjustment | ±20 Mm (with Height‑adjusting Plates) |
| Diameter | 20-30mm |
|---|---|
| Length | 100-300 Mm |
| Thread Type | Partial Thread |
| Finish | Zinc / Hot Dip Galvanized |
| Grade | 4.6/4.8/5.6/5.8/6.8/8.8/10.9/12.9 |
| Material | PA6, PA66, PA66+30% Glass Fiber |
|---|---|
| Tensile Strength | 150MPa (PA66), 170MPa (PA66+30% Glass Fiber) |
| Temperature Range | -40°C To +120°C |
| Melting Point | 260°C-300°C (PA66) |
| Insulation Resistance | ≥1×10¹⁰Ω |
| Material | PA6, PA66, PA66+30% Glass Fiber Reinforced |
|---|---|
| Tensile Strength | 150MPa (PA66), 170MPa (PA66+30% Glass Fiber) |
| Temperature Range | -40°C To +120°C |
| Melting Point | 260°C-300°C (PA66) |
| Insulation Resistance | ≥1×10¹⁰Ω |