Color Paint KP Railway Fastening System ISO 2 - Hole Rail Clip Set Track Parts

Basic Information
Place of Origin: China
Brand Name: ZhongYue
Certification: ISO9001:2015
Model Number: 2 - Hole Rail Clip System
Minimum Order Quantity: 10000sets
Price: Negociable
Packaging Details: according to clients' requirement
Delivery Time: 20-35 working days after received your payment
Payment Terms: T/T, 30% in advance
Supply Ability: 500,000 sets per month
Product Name: Rail Fastening System Application: Railway
Similarity: E / Nabla / SKL / Fist / KP Sample: Available
Surface: Plain (oiled), Oxide Black, Zinc, HDG, Wax, Bitumen, Dacromet
High Light:

railway track fasteners

,

railroad fasteners

Color Paint KP Railway Fastening System ISO 2 - Hole Rail Clip Set Track Parts
 


KP 2-hole Rail Clip Fastening System
 
Technical Parameters

Part name

Type

Material

Finish

Remark

KP clip

2-hole

Q235

Plain oiled

Standard: DIN5906

HS bolt

HS26, HS32

Grade4.6: Q235
Grade5.6: 35#
Grade8.8: 45#

Plain oiled, black oxide, galvanized, hot dip galvanized

Diameter: 22mm or 24mm.
Length: 55mm, 65mm, 75mm, 90mm
Standard: UIC864-2

Hex nut

As ordered

Grade 5: 35#
Grade 8: 45#

Plain oiled, black oxide, galvanized, hot dip galvanized

Standard: DIN985

Double coil spring washer

As ordered

65Mn

Plain oiled, black oxide, galvanized, hot dip galvanized

Standard: UIC864-3

screw spike

M24×150mm
M24 ×160mm
M24 ×180mm
other length

Grade 4.6: Q235
Grade 5.6: 35#
Grade 8.8: 45#

Plain oiled, black oxide, galvanized, hot dip galvanized, Dacromet and sherardized.

Standard: ISO898-1,
UIC864-1
NF F500-50

Base plate

UIC54,UIC60, 50kg rail, 60kg rail,S49 in ordered size

Casting iron QT500-7, QT450-10, or forging low carbon steel or high carbon steel

Plain oiled

Standard: UIC864-6

 
 
Material

 

Material 
Grade 4.6 5.6 8.8 10.9
Material Q235 35# 45# 40Cr
Mechanical properties Tensile strength: ≥400Mpa Tensile strength:≥500Mpa Tensile strength:≥800Mpa Tensile strength:≥1000Mpa
Yield strength:≥240Mpa Yield strength:≥300Mpa Yield strength:≥640Mpa Yield strength:≥900Mpa
Elongation:≥22% Elongation:≥20% Elongation:≥12% Elongation:≥9%
Cold bending: 90 degree without crack
Surface plain (oiled), Oxide black, Zinc, HDG, wax, bitumen, Dacromet, Sherardizing

 
Note ( 8.8 as a sample)
the first 8: tensile strength of material 45# is 800MPa;
the second 0.8: the yield ratio is 0.8;
the yield strength of material 45# is 800MPa x 0.8 = 640 MPa.

 
Color Paint KP Railway Fastening System ISO 2 - Hole Rail Clip Set Track Parts 0
 
Surface Treatment

  1. plain (oiled)
  2. color paint
  3. oxide Black (most choice)
  4. galavazing
  5. DHG

 

Inspection machine

  1. Brinell Hardness Tester
  2. Carbon and Sulfur Analyzer
  3. Rockwell Hardness Machine
  4. Automatic Impact Testing Machine
  5. Metallographic Microscope
  6. Automatic High-speed Analyzer
  7. Fatigue Testing Machine
  8. Metallographic Specimen Polishing Machine
  9. Metallographic Specimen Pointing Machine

 

Package
1. 25kg per double layer woven bag+ free fumigation wooden pallet
    36bags/pallet,
    24pallets/container
2. Keg
3. in according with your request
 


Application
Color Paint KP Railway Fastening System ISO 2 - Hole Rail Clip Set Track Parts 1
Color Paint KP Railway Fastening System ISO 2 - Hole Rail Clip Set Track Parts 2
 
 
Similarity

 

  1. E CLIP SYSTEM
  2. NABLA SYSTEM
  3. SKL 1 / 2 / 3 / 12 / 14 CLIP SYSTEM
  4. FIST CLIP SYSTEM
  5. SPECIAL CLAMP SYSTEM